Increased efficiencies of the copolymers with fluoro groups in vinylene units

Metadata Downloads
Abstract
New electroluminescent copolymers with fluoro groups in the vinylene unit, poly(9,9-dihex ylfluorene-2,7-vinylene-co-p-phenylenedifluorovinylene) (PFVPDFV), have been synthesized by the GILCH polymerization. The fluoro groups were introduced on vinylene units to increase the electron affinities of the copolymers. The PFVPDFVs exhibit absorption spectra with maximum peaks at 371-413 nm. The maximum absorption peak at 413 nm of PFVPDFV1 was blue-shifted with a larger amount of the PDFV. In the PL spectra of PFVPDFVs, as the PDFV content increases up to 50% in the copolymer system, the fwhm was decreased by 4-38 nm as compared to PFV. The HOMO energy levels of the copolymers were about 5.25-5.50 eV, and the LUMO energy levels were about 2.67-2.97 eV. The polymer LEDs (ITO/PEDOT/polymer/A1) of PFVPDFVs showed emission with maximum peaks at around 472-538 nm. By adjusting the feed ratios of PDFV in the copolymers, it was possible to tune the emission colors from greenish yellow to orange depending on the obtained CIE coordinates. The luminescence efficiencies of the copolymers at room temperature are about 0.1-1.47 cd/A. PFVPDFV3 showed the maximum brightness of 4870 cd/m(2) and the highest luminescence efficiency of 1.47 cd/A. The introduction of up to 50% of PDFV in PFVPDFVS can enhance the device performance to result in high current density, brightness, and efficiency due to the increased electron injection ability caused by the presence of fluoro groups in the vinylene units.
Author(s)
Jin, YoungeupKim, KwanghyunPark, Sung HeumSong, SuheeKim, JaehongJung, JaeyeonLee, KwangheeSuh, Hongsuk
Issued Date
2007-09
Type
Article
DOI
10.1021/ma071074z
URI
https://scholar.gist.ac.kr/handle/local/17597
Publisher
American Chemical Society
Citation
Macromolecules, v.40, no.19, pp.6799 - 6806
ISSN
0024-9297
Appears in Collections:
Department of Materials Science and Engineering > 1. Journal Articles
공개 및 라이선스
  • 공개 구분공개
파일 목록
  • 관련 파일이 존재하지 않습니다.

Items in Repository are protected by copyright, with all rights reserved, unless otherwise indicated.