Task-specific polymeric membranes to achieve high gas-liquid mass transfer

Abstract

In the current study, Polyimide (P84)-based polymeric membranes were fabricated and used as spargers in the bubble column reactor (BCR) to get a high gas-liquid mass transfer (GL-MT) rate of oxygen in water. Different polymeric membranes were fabricated by incorporating polyvinyl pyrrolidone (PVP) as a porogen and a Zeolitic Imidazolate Framework (ZIF-8) to induce high porosity and hydrophobicity in the membranes. The GL-MT efficiency of membranes was evaluated by measuring the overall volumetric mass transfer coefficient (kLa) of oxygen in air. The kLa of O2 (in air) was measured by supplying the gas through a fixed membrane surface area of 11.94 cm2 at a fixed gas flow rate of 3L/min under atmospheric pressure. The results revealed that adding porogen and ZIF-8 increased the porosity of the membranes compared to the pure polymeric membranes. In comparison, the ZIF-8 (3 wt%) based membrane showed the highest porosity (80%), hydrophobicity (95° contact angle) and kLa of oxygen in air (241.2 h−1) with 78% saturation in only 60 s. ZIF-8 based membranes showed the potential to increase the amount of dissolved oxygen in BCR by reducing the bubble size, increasing the number of bubbles, and improving the hydrophobicity. The study showed that ZIF-8 based membrane diffusers are expected to produce high GL-MT in microbial syngas fermentation. To the best of our knowledge, this is the first study on the fabrication and application of polymeric membranes for GL-MT applications. Further research should be conducted under real fermentation conditions to assess the practicality of the system to support substrate utilization, microbial growth, and product formation. © 2022 Elsevier Ltd